Abid Karim

• The electrodynamics of the spin density wave (SDW) state for the parent SrFe2As2 and doped SrCo1.9Fe0.1As2 pnictides were studied by high–pressure infrared spectroscopy at low temperatures. The pressure–temperature phase diagram was established and electronic correlations were calculated from the spectral weight analysis. The infrared properties of EuB6 were studied under high pressure and low temperatures. The plasma frequency was increased substantially with application of high pressure both in paramagnetic and ferromagnetic states. The ratio of the plasma frequencies for ferromagnetic to the paramagnetic states were calculated at 100 K and 5 K. The calculated ωp, 5K / ωp, 100K ratio decreases with increasing pressure. This means that the magnetic blue shift is diminishing with increasing pressure, which is a remarkable agreement with the earlier calculations done by Kunes et al [81] and Kim et al [79].
• Die Elektrodynamik des Spindichtewellen-Zustandes (SDW) der Stammverbindung SrFe2As2 und des dotierten SrCo1.9Fe0.1As2 Pniktids wurde mittels Infrarotspektroskopie unter hohen Drücken und tiefen Temperaturen untersucht. Das Druck-Temperatur-Phasendiagramm wurde ermittelt und die elektronischen Korrelationen aus der Analyse des spektralen Gewichts berechnet. Die Infraroteigenschaften von EuB6 wurden unter hohen Drücken und tiefen Temperaturen untersucht. Die Plasmafrequenz wurde durch Applizierung von Druck sowohl im paramagnetischen als auch im ferromagnetischen Zustand deutlich erhöht. Das Verhältnis der Plasmafrequenzen im paramagnetischen und ferromagnetischen Zustand wurde bei 100 K und 5 K berechnet. Das berechnete ωp, 5K / ωp, 100K-Verhältnis verringert sich mit zunehmendem Druck. Das bedeutet, dass die magnetische Blauverschiebung mit zunehmendem Druck abnimmt, was durch frühere Berechnungen von Kunes et al. [81] und Kim et al. [79] bestätigt wird.