The recent discovery of a stable γ'-phase in Co-based superalloys opened up a pathway for the development of a new high temperature material class, which is similar in microstructure and properties to the modern γ'-hardened Ni-based superalloys. In this work, the first attempt was done to check the influence of several for Ni-based superalloys typical alloying elements on the properties of the new Co-based superalloys. It became clear that the basic characteristics of the first experimental alloys are similar to those of the γ'-hardened Ni-based alloys. The results of the multinary experimental alloys show that, based on the insight gained so far, targeted alloy development is possible. These materials have the potential to be used as disc materials in turbines.

Die vor wenigen Jahren entdeckte Möglichkeit der γ'-Ausscheidungshärtung in Kobaltlegierungen eröffnete die Entwicklung einer neuen, den modernen γ'-gehärteten Nickelbasis-Superlegierungen mikrostrukturell vergleichbaren Legierungsklasse. Im Rahmen dieser Arbeit wurde der Einfluss mehrerer, für Nickellegierungen typischer Legierungselemente auf die Hochtemperatureigenschaften der neuen Kobaltlegierungen untersucht. Es zeigte sich, dass die grundlegenden Eigenschaften erster Experimentallegierungen den γ'-gehärteten Nickelbasis-Superlegierungen prinzipiell ähnlich sind. Die Ergebnisse zu den ersten multinären Experimentallegierungen zeigen, dass anhand der bisher gewonnenen Erkenntnisse eine gezielte Legierungsentwicklung möglich ist. Diese Materialien haben das Potential als Scheibenwerkstoffe in Turbinen eingesetzt zu werden.