Abstract
We report on the direct comparison of single-crystal and ceramic Yb3+:Lu203 gain media with respect to emission spectra, fluorescence lifetime, depolarization, and laser performance in a continuous-wave thin-disk laser oscillator. The most efficient laser operation was achieved with a single-crystal disk in multimode operation with a slope efficiency of 72.1% and an average output power of 997 W. At the same temperature level, a ceramic disk delivered 861 W with a slope efficiency of 68.6%. In fundamental-mode operation, the highest average power of 360 W and highest optical efficiency of 41.3% were obtained with a ceramic disk. For the single-crystal disk, the fundamental-mode output power was limited to 113 W at an optical efficiency of 29%, potentially due to stress within the crystal.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
The sesquioxide crystal Yb3+:Lu2O3 is a gain medium with excellent potential for thin-disk lasers operating at high average powers. Efficient pumping is possible thanks to its narrow but high absorption peak with an absorption cross-section of σabs = 3.1·10−20 cm2 at a wavelength of 976 nm [1]. The quantum defect amounts to only 5.6% with a laser emission centered at 1034 nm [2]. In addition to the low heat generation, the thermal conductivity of Yb:Lu2O3 amounts to 12 W/mK, which is almost twice the value of the heat conductivity of the well-established laser crystal Yb:YAG (both at the same Yb-ion density of 8·1020 cm−3) [1]. Additionally, Yb:Lu2O3 exhibits a comparatively broad emission bandwidth of 13 nm full width at half maximum (FWHM) [3] which is especially interesting for mode-locking to obtain pulse durations in the order of 100 fs and below.
Yet, the high melting point of 2450 °C [2] is a challenge for the growth of Yb:Lu2O3 single crystals. Thus, the availability of high-quality single crystals with sizes exceeding about 10 mm is very limited. Larger laser-grade Yb:Lu2O3 samples can be produced by means of ceramic manufacturing techniques as shown in [4], where the sintering temperatures are significantly lower with maximum at 1700 °C.
When comparing the record thin-disk laser results for ceramic and single crystalline Yb:Lu2O3, the highest overall slope efficiency of 85% was attained with a single crystal together with an output power of 301 W [1]. The highest slope efficiency achieved with a ceramic Yb:Lu2O3 disk was 74% with a maximum output power of 16 W [5]. The highest ever-published output power of 1.19 kW from a Yb:Lu2O3 laser so far was achieved with a ceramic disk and the slope efficiency amounted to 65% [6]. The highest output power published for a single-crystal Yb:Lu2O3 disk is 670 W and the corresponding slope was 80% [7]. These cited publications are all devoted to either the ceramic or the single-crystal disks which impedes a detailed comparison.
We, therefore, report on a comparative study of single-crystal and poly-crystalline ceramic Yb:Lu2O3 gain media with regard to their emission spectra, fluorescence lifetime, depolarization, and laser performance in a continuous- wave (cw) multimode (MM) and fundamental transverse-mode (FM) thin-disk oscillator.
2 Disk characterization
2.1 Materials
Three different Yb3+-doped Lu2O3 disks were investigated—a 3 at.% Yb:Lu2O3 single-crystal disk (referred to as “SC 3%” in the following), a 4 at.%- and a 5 at.% Yb:Lu2O3 poly-crystalline ceramic disk (referred to as “PC 4%” and “PC 5%”, respectively). Photographs of the three samples are shown in Fig. 1. The disk SC 3% was grown using the heat-exchanger method at the ILP Hamburg [8] and was polished to a thickness of 115 µm. The two ceramic samples were fabricated by the Jiangsu Normal University in Xuzhou, using a combination of vacuum sintering and hot isostatic pressing of high-purity powders, similar to the approach described in [4]. The thickness of the disk PC 4% was 125 µm and that of disk PC 5% was 100 µm. The grain size of the ceramics ranged from 5 µm to 40 µm and both samples were free of pores. All three disks had a diameter of 11 mm and were anti-reflection (AR) coated at their front face and highly reflective (HR) at their rear face for both the pump and the laser wavelengths. Each disk was glued on a water-cooled diamond heat sink for efficient heat removal.
Yb:Lu2O3 thin disks glued on diamond heat sinks: a disk SC 3%, b disk PC 4%, c disk PC 5%
2.2 Emission spectra
The emission spectra were measured by exciting the disks with a cw diode laser with a spectrum centered at a wavelength of 976.5 nm and a spectral width of 0.4 nm FWHM. The diode laser was focused on the disks with a spot size of 5.5 mm under an angle of 32° and a power density of 21 W/cm2. The emission spectra were recorded by a spectrometer covering the wavelength range between 900 and 1100 nm, coupled with a multimode fiber facing under an angle of 0° toward the disks.
The peak-normalized emission spectra shown in Fig. 2 exhibit no significant difference between the three samples. The emission peaks of all the three samples are centered at a wavelength of 1033 nm.
Peak-normalized cw emission spectra of the three Yb:Lu203 samples recorded during excitation at a wavelength of 976.5 nm
2.3 Fluorescence lifetime
The fluorescence lifetime was measured immediately after turning off the excitation (falltime < 5 µs) using a spectral filter (transmission wavelength 1020 nm–1040 nm) and an ultrafast photodiode (falltime < 50 ps). The resulting decay curves are shown in Fig. 3.
Measured fluorescence decay and exponential fits (black dashed): a decay during the first 5 ms after turning off the excitation. b Excerpt showing the first 2 ms
The fluorescence lifetimes were measured to amount to 988 µs for disk SC 3%, 914 µs for disk PC 4%, and 903 µs for disk PC 5%. The lifetime measured for the single crystal SC 3% is close to the value of 975 µs previously reported for single-crystal Yb:Lu2O3 [8]. The lifetimes of the ceramic samples are about 8% shorter than the one of the single-crystal sample but significantly longer than the values previously reported for Yb:Lu2O3 ceramics, of 750 µs [5] and 710 µs [9]. This indicates an improved purity of the present ceramic samples.
Nevertheless, the shortened lifetimes of both ceramics in comparison to the single-crystal sample indicate the presence of quenching of the dopant’s upper states and parasitic processes within the ceramic samples. The shortened lifetimes may be associated with higher losses during laser operation which is consistent with higher resonator losses measured for the ceramics, as will be shown in Sect. 3.1 (see Fig. 6).
2.4 Depolarization images
To assess the presence of stress [10] within the otherwise isotropic material [3], the depolarization of the disks was measured by illuminating the samples at normal incidence with a Nd:YAG laser beam with a power of 44 mW at a wavelength of 1064 nm in a crossed-polarizers arrangement as depicted in Fig. 4a. The signal of the camera was calibrated with the two polarizers set to a parallel orientation (100% transmittance) and using a highly reflective mirror and a calibrated attenuation filter to replace the Yb:Lu2O3 disk.
a Crossed-polarizer arrangement to measure the depolarization. The cube beam splitter (BS) is non-polarizing. d Depolarization images of the three Yb:Lu2O3 disks. b disk SC 3%, c disk PC 4%, d disk PC 5%
The depolarization images of the three different disks are shown in Fig. 4b, c, and d. For each sample, four images were taken with the disks rotated by 0°, 45°, 90°, and 135° around the z-axis, with respect to an arbitrarily chosen initial angle of 0°. The white arrows in Fig. 4b–d represent the orientation of the input polarization, and the red-dashed arrows show the relative orientation of the disks with respect to their initial orientation.
The highest average amount of depolarization of 0.081% was observed for the disk SC 3%. The lowest average depolarization of 0.013% was found for the disk PC 4%. The one of the disk PC 5% was measured to be 0.03%.
The spatial distribution of the depolarization observed in the cross-sectional area of the disk PC 5% is typical for a radially symmetric stress distribution [11] and may be the result of an inhomogeneous pressure distribution during sintering.
The dependence of the depolarization on the orientation of the disk exhibited by the sample SC 3% indicates a correspondingly asymmetric distribution of the stress in the single crystal, which may be caused by asymmetric crystallization conditions during the growth.
Disk PC 4% shows a uniform distribution of depolarization. Hence, this disk is the most suitable one for laser operation where polarization preservation is of importance.
3 Laser experiments
3.1 Multimode operation
The three different Yb:Lu2O3 gain media were first operated in a cw MM thin-disk oscillator, with the experimental setup shown in Fig. 5. Each disk was mounted inside a multi-pass pump module that allows for 24 passes of the pump light through the crystal (12 reflections at the rear side of the disk). The diameter of the pump spot on the disk was set to 5.5 mm. A spectrally stabilized fiber-coupled diode laser with an output power of 2 kW and a 0.4 nm wide emission spectrum (FWHM) centered at a wavelength of 976.5 nm was used for pumping. The absorption of the pump light after 24 passes through the disk was measured by inserting a thin uncoated glass plate at an angle of 45° into the beam path outside the pump module (see Fig. 5). The absorption at each maximum pump power was 91% for disk SC 3% and 96.5% for disk PC 4% and PC 5%, respectively. The surface temperature of the disk was recorded with a thermal camera.
Setup for MM operation: Yb:Lu2O3 disk (green) mounted on a water-cooled diamond heat sink, multi-pass pump module, and V-shaped laser cavity. For the sake of clarity, the drawing of the pump module does neither show all optical components nor the individual bam paths. Power meters (PM) are depicted in blue
The V-shaped MM cavity was formed by a concave HR end mirror (radius of curvature RoC = 3 m), the disks (RoC = 3.8 m) and a plane output coupler (OC). This cavity generated a laser beam with a beam propagation factor of M2 = 15. The wavelength of the laser emission was centered at 1033 nm in all experiments.
First, the resonator losses are measured after Caird et al. [12], by varying the transmission of the OCs and plotting the inverse slope efficiency against the inverse transmission rate, as shown in Fig. 6. A linear fit is applied to the data points and its slope corresponds to the resonator losses. Losses due to non-perfect coatings are estimated to be around 0.05% in this cavity; hence, the measured resonator loss is mainly a loss due to the Yb:Lu2O3 disks.
Caird analysis of the Yb:Lu2O3 disks in continuous-wave multimode operation. The linear fits are applied to the data points without a bracket
The lowest resonator losses are measured for disk SC 3% with 0.13%. For the ceramic disks, the resonator losses are significantly higher with 0.48% for disk PC 4% and 0.53% for disk PC 5%. This is consistent with the shortened lifetime of the ceramics which indicates parasitic loss processes. Additionally, we suspect scattering at the grain boundaries to contribute to the higher losses for the ceramics.
Furthermore, the Caird analysis gives the OC transmission with the highest slope efficiency which is found to be 3% for disk SC 3%, and 4% for the disks PC 4% and PC 5%.
The high-power MM laser test was conducted with the respective optimum OCs. The output powers and optical efficiencies are shown in Fig. 7 as a function of the absorbed pump power. The corresponding peak surface temperatures on the laser disks during MM operation are shown in Fig. 8 as a function of the absorbed power density. To minimize the risk of a thermally-induced damage, each disk was pumped up to a maximum surface temperature of 100 °C (see Fig. 8).
Output power (circles), linear fit (dashed line), and optical efficiency (triangles) versus absorbed pump power in cw MM operation
Maximum surface temperature on the disks versus absorbed power density. Linear interpolations (dashed lines) were fitted to the data points. The inset exemplarily shows the thermal image of disk PC 5%
The highest slope efficiency of 72.1% and the highest output power of 997 W were obtained with the disk SC 3%.
An output power of 861 W with a slope efficiency of 68.6% was reached with the disk PC 4%. The disk PC 5% delivered an output power of 729 W with a slope efficiency of 66.9%.
It is assumed that residual losses within the ceramic disks are the main reason for the slightly reduced slope efficiencies compared to disk SC 3%.
Yet it is to be noted, that all disks do not exploit the maximum possible slope efficiency, which would only be limited by the quantum defect, and hence amount to 94.5%. Thus, there are still loss mechanisms that reduce the maximum achievable slope efficiency and that are not yet fully understood.
The lowest temperature rise was observed with the disk SC 3% with a slope of 12.4 K/(kW/cm2), followed by disk PC 4% with a slope of 13.1 K/(kW/cm2) and disk PC 5% with a slope of 14.4 K/(kW/cm2).
A correlation between the temperature rise and the laser efficiency can be observed. Disk SC 3% showed the lowest temperature rise and at the same time the highest slope efficiency during MM laser operation. The lowest slope efficiency and the highest temperature rise were found with disk PC 5%. In fact, a lower efficiency in laser operation means that a lower fraction of the absorbed pump power is extracted out of the gain medium. Thus, more energy can be converted into heat.
Also, the ceramics shortened lifetime and relatively high resonator losses are consistent with their increased temperature rise, since both indicate the presence of non-radiative transitions of excited ions which would also contribute to the heating.
3.2 Fundamental-mode operation
A sketch of the setup used for fundamental-mode operation is shown in Fig. 9. The cavity consisted of a plane OC, the laser disk, two plane HR folding mirrors, and a concave HR end mirror with a radius of curvature of 1 m. The same output coupling as for the MM operation was used, i.e., 3% for disk SC 3% and 4% for disk PC 4% and disk PC 5%. The end mirror was placed on a linear stage to fine-tune the ratio between the diameter of the laser mode and the diameter of the pump spot by adapting the mirror’s axial position.
Setup for fundamental-mode operation. For the sake of clarity, the drawing of the pump module does neither show all optical components nor the individual bam paths
The output power and optical efficiency obtained in fundamental-mode operation are shown in Fig. 10 as a function of the absorbed pump power.
Output power (circles), linear fit (dashed line), and optical efficiency (triangles) versus absorbed pump power in cw FM operation
The corresponding M2 values are shown in Fig. 11 as a function of the laser output power. With a nominal ratio between the diameter of the fundamental mode and the diameter of the pump spot of 0.8, the M2 values were kept below 1.2 across the entire power range for all three disks.
Beam propagation factor M2 versus laser output power. The insets show exemplary far-field intensity distributions of the output beams generated using the three laser disks, each at maximum output power
The highest output power of 360 W together with a slope efficiency of 49.6%, an optical efficiency of 41.3%, and M2 = 1.1 was achieved with disk PC 4%. An output power of 190 W and M2 = 1.1 was achieved with disk PC 5%, with a slope efficiency of 41.6% and an optical efficiency of 32.4%.
For both ceramic disks, further power increase was limited due to thermal lensing, by reaching the stability limits of the fundamental-mode resonator. The thermal lens was measured during fundamental-mode operation by means of a UV interferometer. It amounted to −89 mdpt/kW for disk PC 5% and to −39 mpdt/kW for disk PC 4%. Consequently, the power limitation of this cavity was reached at a lower power with disk PC 5%. Note that the negative sign of the thermal lenses arise from the fact that the cross-sectional temperature distribution shows a dip in the center during fundamental-mode operation due to the Gaussian-shaped extraction. Together with a positive dn/dT and dl/dT [13], this leads to a negative thermal lens in our case.
With the the single-crystal disk SC 3%, an output power of 113 W, a slope efficiency of 43%, and an optical efficiency of 29.0% were obtained at a M2 = 1.2. In contrast to the ceramic disks, the power achieved with disk SC 3% was limited by an unexpected instability of the mode and not by the resonator instability as would be expected due to thermal lensing at higher powers.
It was observed that the position of the laser mode was subject to a lateral oscillation with respect to the pump spot without any changes in the pump power or the alignment of the setup. The higher the pump power, the stronger this effect was, eventually leading to the collapse of the laser operation.
Figure 12a shows a photograph of the aligned state of disk SC 3% at its maximum output power in fundamental-mode operation and Fig. 12b shows a sequence of follow-up images recorded at 1 Hz.
Photographs of the disk SC 3% during fundamental-mode operation: a initial alignment. b Follow-up images recorded at 1 Hz showing the motion of the mode. The laser operation collapsed in the image on the bottom right, as can be seen due to the lack of the laser-mode imprint
It is worth mentioning that the eccentric alignment of the pump spot with respect to the disk was chosen intentionally, as the described effect was the weakest at this position.
It is assumed that this behavior is related to the relatively strong and asymmetric stress-induced birefringence that was observed during the measurement of the depolarization of this disk, but further investigations will be required to clarify this point.
4 Conclusion
In conclusion, it was found that the investigated ceramic and single-crystal Yb:Lu2O3 disks exhibit comparable spectroscopic properties, indicating a high purity of the ceramic samples. The lower stress-induced birefringence was found to be a significant advantage of ceramic Yb:Lu2O3 disks. In multimode laser operation, all disks delivered kilowatt-class output powers with the highest slope efficiency of 72.1% for the single-crystal and 68.8% for the ceramic disks. Residual scattering losses in the ceramics are suspected to cause this difference. In fundamental-mode laser operation, the ceramics outperformed the single crystal with regard to the output power, potentially due to the lower stress-induced depolarization in the ceramics.
Future work will be dedicated to investigate the suitability of the Yb:Lu2O3 ceramics for mode-locked thin-disk lasers.
References
R. Peters, C. Krankel, S. Fredrich-Thornton, K. Beil, K. Petermann, G. Huber, O. Heckl, C. Baer, C. Saraceno, T. Sudmeyer, U. Keller, Appl. Phys. B 102, 509–514 (2011)
K. Petermann, L. Fornasiero, E. Mix, V. Peters, Opt. Mater. 19(1), 67–71 (2002)
V. Petrov, K. Petermann, U. Griebner, V. Peters, J. Liu, M. Rico, P. Klopp, G. Huber. Laser source and system technology for defense and security II 6216, 62160H. SPIE, (2006)
D. Yin, J. Wang, Y. Wang, P. Liu, J. Ma, X. Xu, D. Shen, Z. Dong, L.B. Kong, D. Tang, J. Eur. Ceram. Soc. 40(2), 444–448 (2020)
J. Sanghera, J. Frantz, W. Kim, G. Villalobos, C. Baker, B. Shaw, B. Sadowski, M. Hunt, F. Miklos, A. Lutz, I. Aggarwal, Opt. Lett. 36(4), 576–578 (2011)
S. Esser, C. Rohrer, X. Xu, J. Wang, J. Zhang, T. Graf, M. Abdou Ahmed, Opt. Lett. 46(24), 6063–6066 (2021)
B. Weichelt, K.S. Wentsch, A. Voss, M. Abdou Ahmed, T. Graf, Laser Phys. Lett. 9(2), 110–115 (2012)
R. Peters, C. Krankel, K. Petermann, G. Huber, J. Cryst. Growth 310(7), 1934–1938 (2008)
Z. Liu, G. Toci, A. Pirri, B. Patrizi, Y. Feng, J. Wei, F. Wu, Z. Yang, M. Vannini, J. Li, J. Adv. Ceram. 9, 674–682 (2020)
L.N. Soms, A.A. Tarasov, V.V. Shashkin, Sov. J. Quantum Electron. 10(3), 350 (1980)
J. Dominik, M. Scharun, B. Dannecker, V. Buhner, K. Ertel, D. Bauer, T. Dekorsy, Appl. Opt. 61(17), 4986–4992 (2022)
J.A. Caird, S.A. Payne, P.R. Staber, A.J. Ramponi, L.L. Chase, W.F. Krupke, IEEE J. Quantum Electron. 24(6), 1077–1099 (1988)
I.L. Snetkov, D.E. Silin, O.V. Palashov, E.A. Khazanov, H. Yagi, T. Yanagitani, H. Yoneda, A. Shirakawa, K. Ueda, A.A. Kaminskii, Opt. Express 21, 21254–21263 (2013)
Funding
Open Access funding enabled and organized by Projekt DEAL. This study was supported by Deutsche Forschungsgemeinschaft (No. 410806665) and National Natural Science Foundation of China (No. 61861136007).
Author information
Authors and Affiliations
Contributions
SE performed all measurements and wrote the manuscript. XX, JW and JZ where involved in the fabrication of the ceramics. TG and MAA assisted in the preparation of the manuscript. All authors reviewed the manuscript.
Corresponding author
Ethics declarations
Conflict of interest
The authors declare no conflicts of interest.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Esser, S., Xu, X., Wang, J. et al. Single-crystal and ceramic Yb:Lu2O3 gain media for thin-disk oscillators. Appl. Phys. B 129, 160 (2023). https://doi.org/10.1007/s00340-023-08103-x