Abstract
A series of glass samples was prepared from mixtures of Na2B4O7 and V2O5. Measurements were made for infrared absorption and optical absorption spectra as a function of V2O5 content up to 10 mol%. The addition of V2O5 did not introduce any new absorption band as compared with the infrared spectrum of pure sodium tetraborate glass. The addition of V2O5 shifted the optical absorption edges towards lower energies, and introduced a new absorption band as compared with the optical absorption of pure Na2B4O7 glass. Differential scanning calorimetry as a function of V2O5 content was also measured.
Similar content being viewed by others
References
N. F. Mott and E. A. Davis, “Electronic processes in noncrystalline materials” (Oxford University Press, Oxford, 1971).
R. H. Sands, Phys. Rev. 99 (1955) 1222.
N. F. Mott, J. Non-Cryst. Solids 1 (1968) 1.
L. W. Herron and C. G. Bergeron, Phys. Chem. Glasses 19 (1978) 89.
A. Paul and R. W. Douglas, ibid. 6 (1965) 212.
N. F. Borrelli, B. D. McSwain and Gouq-Jen Su ibid. 4 (1963) 11.
J. S. Berkes and W. B. White, ibid. 7 (1966) 191.
H. Bach and J. A. Duffy, ibid. 4 (1981) 86.
A. Paul, ibid. 13 (1972) 194.
A. A. Kutub, A. E. Mohamed-Osman and C. A. Hogarth, J. Mater. Sci. 21 (1986) 3859.
A. A. Kutub, K. A. Maghrabi and C. A. Hogarth, ibid. 22 (1987) 2199.
A. M. Sanad, I. Kashif, A. M. Abou Al-Azm, M. A. Khaled and H. Farouk, ibid. 21 (1986) 230.
A. M. Sanad, I. Kashif, A. A. El-Sharkawy and A. A. El-Saghier, ibid. 21 (1986) 3483.
E. E. Khawaja, F. Tegally, J. S. Hwang, A. S. W. Li and A. A. Kutub, ibid. 20 (1985) 3074.
M. M. Ahmed and C. A. Hogarth, J. Mater. Sci. Lett. 2 (1983) 254.
E. E. Khawaja and G. D. Khattak, Phys. Stat. Solidi. (a) 93 (1986) 621.
C. A. Hogarth and M. M. Ahmed, J. Mater. Sci. Lett. 2 (1983) 649.
S. A. Kutolin, G. S. Bolinkva, O. M. Kolenko, R. N. Samoilova and M. I. Dokuchaeva, Inorg.Mater. (USA) 10 (1974) 550.
S. A. Kulieva, P. F. Rza-Zade, K. L. Ganf and N. P. Luzhnaga, ibid. 10 (1978) 2013.
A. A. Kutub, A. Y. Bargawi, K. A. Maghrabi and C. A. Hogarth, J. Mater. Sci. 22 (1987) 3607.
J. L. Piguet and J. E. Shelby, J. Amer. Ceram. Soc. 68 (1985) 450.
A. A. Kutub, J. Mater. Sci. 23 (1988) 2495.
B. D. McSwain, N. F. Borrelli and G. J. Su, Phys. Chem. Glasses 4 (1963) 1.
A. A. Kutub, Int. J. Elect. 67 (1989) 65.
Y. Limb and R. F. Davis, J. Amer. Ceram. Soc. 62 (1978) 403.
N. H. Ray, J. Non-Cryst. Solids 15 (1974) 423.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kutub, A.A., Al-Ghorabie, F.H. & Natto, S.S. Some optical and differential scanning calorimetry studies of sodium tetraborate glasses containing vanadium oxide. J Mater Sci 26, 4421–4426 (1991). https://doi.org/10.1007/BF00543662
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF00543662